High-Density Polyethylene (HDPE) with Cross Lamination Strength Cross-Laminated Film -60f

• Customization: Available
• Thickness: 0.09-0.265 mm
• Width: 900-1200 mm
• Model NO.: Strength Cross-Laminated Film -60F
• Sleeve ID: 76 mm
• Tensile Strength: ≥30 MPa
• Maximum Tension: ≥200 (N/50mm)
• Transport Package: Bubble Membrane + Tray
• Specification: Thickness 0.09-0.265 mm
• Trademark: Upass
• Origin: China

Product Description

Strength Cross-Laminated Film -60F



Material and Structure: High-density polyethylene(HDPE) with cross lamination

Colors: blue, black, gray, white, green, etc

Features:
High Strength Cross Laminated HDPE Film - SDM-60F is an anti-slip cross laminated film, and the anti-slip layer can be made into various patterns according to customer requirements. At the same time, it also has the characteristics of a cross laminated film, which is stable and does not deform; High strength and high elongation; Tear resistance; High and low temperature resistance; Has unique puncture resistance; Self healing and sustained tear resistance, as well as excellent water tightness of the nail rod; Has the ability to resist ultraviolet radiation.

Usage: Used as surface material for waterproofing membranes, tapes, underlayment, special packaging, label markets, etc.

Advantages:

1. High tear performance, and have good printing effects.
2. The biggest advantage is anti-slip, suitable for waterproofing membranes on slopes and sloping roofs, and construction safety.

Data Sheet:

Item		Unit	Performance Index
Thickness		mm	0.09-0.265
Width		mm	900-1200
Sleeve ID		mm	76
Frictional Coefficient		/	≥0.6
Tensile Properties	Tensile Strength	Mpa	≥50
	Maximum Tension	(N/50mm)	≥200
	Elongation at Maximum Tension	%	≥250
	Elongation at Break	%	≥250
Nail Rod Tear Strength		N	≥60
Dimensional Stability at 90 ºC		%	≤1.5%
Tear Strength		N	≥25
Heat Resistance(70 ºC, 24h)		ºC	After applying asphalt, the maximum curling of the polymer film or tire base edge shall not exceed 1/4 of the edge length
Low Temperature Flexibility		ºC	-30 ºC, no cracks, no layering
Aging Test (70 ºC, 7days)	Appearance		No bubbles, no layering
	Tensile Retention Rate	%	≥90
	Elongation Retention Rate	%	≥80