Stable and Non Deformable Resist Ultraviolet Radiation Strength Cross Laminated Film 60n

• Thickness: 0.09-0.265 mm
• Width: 900-1200 mm
• Sleeve ID: 76 mm
• Tensile Strength: ≥30 MPa
• Maximum Tension: ≥200 (N/50mm)
• Transport Package: Bubble Membrane + Tray
• Model NO.: Strength Cross Laminated Film 60N
• Trademark: Upass
• Origin: China

Product Description

Strength Cross Laminated Film 60N




Material and structure: high-density polyethylene
Colors: blue, black, gray, white, green, etc
Characteristics: Stable and non deformable; High strength and high elongation; Tear resistance; High and low temperature resistance; Has unique puncture resistance; Self healing and sustained tear resistance, as well as excellent water tightness of the nail rod; Has the ability to resist ultraviolet radiation
Usage: Used for building waterproofing, special packaging, label markets, etc.
Advantages: Meet the PE type I and II indicators of self-adhesive rolls, and the E type indicators of wet laid rolls, with high tear performance and good printing effect. The biggest advantage is environmental protection, smooth film surface without curling edges, and high nail rod tear.
    
Data Sheet:

Item		Unit	Performance Index
Thickness		mm	0.09-0.265
Width		mm	900-1200
Sleeve ID		mm	76
Tensile Properties	Tensile Strength	Mpa	≥50
	Maximum Tension	(N/50mm)	≥250
	Elongation at Maximum Tension	%	≥250
	Elongation at Break	%	≥250
Nail Rod Tear Strength		N	≥110
Dimensional Stability at 90 ºC		%	≤1.5%
Tear Strength		N	≥25
Heat Resistance(70 ºC, 24h)		ºC	After applying asphalt, the maximum curling of the polymer film or tire base edge shall not exceed 1/4 of the edge length
Low Temperature Flexibility		ºC	-30 ºC, no cracks, no layering
Aging Test (70 ºC, 7days)	Appearance		No bubbles, no layering
	Tensile Retention Rate	%	≥90
	Elongation Retention Rate	%	≥80